Theoretical and Experimental Analyses of Thermal Conductivity of the Alumina-Mullite System |
Mr. Shota Ito |
Kagoshima university |
|
The thermal conductivity of the three phase system of alumina-mullite-pore was calculated by a theoretical equation developed [1,2] in this research group, and compared with the experimental results. The pores in the sintered composite were treated as one phase. A theoretical thermal conductivity of alumina-mullite-pore system was calculated for two cases : mullite continuous phase and alumina continuous phase. Figure 1 shows the measured and calculated thermal conductivities for the alumina-mullite-pore system. The measured conductivity of the composite with 0.5-25 % porosity was in accordance with the calculated value for the mullite continuous phase. No grain size effect of mullite particles on the thermal conductivity was measured in the range of 1-50 ¥ìm. This result is also explained by the developed model. |
Acknowledgements : |
|
Address: Rm. 104, Changwon Exhibition & Convention Center(CECO), 362, Wonidae-ro, Uichang-gu, Changwon City, Gyeongsangnam-do, Korea
Tel : +82-55-212-1337, Fax : +82-55-212-1331, E-mail : kj-ceramics31@changwon.ac.kr
copyright@GNA International All rights reserved. since 2006