The influence of Ag interlayer on the electrical and optical properties of ZTO/Ag/ZTO multilayer films |
Mr. Taekyung Gong |
University of Ulsan |
|
Silver (Ag) intermediated ZTO ( ZTO/Ag/ZTO ; ZAZ ) films were deposited with RF and DC magnetron sputtering on a glass substrate. The thickness of Ag interlayer was set at 5, 10 and 15 nm, respectively. The electrical and optical properties of the films were investigated with the Hall effect measurement and the UV-visible spectroscopy[1, 2]. The observed electrical and optical properties were dependent on the thickness of the Ag interlayer. The resistivity of the films with 15 nm thick Ag interlayer decreased as low as 8.5 x 10-5 ¥¨ª cm and the highest optical transmittance of 83.2 % was also observed in that films. The ZAZ films with a 15 nm thick Ag interlayer showed a higher optical and electrical performance than another ZAZ films prepared in this study |
Acknowledgements : This research was financially supported by the Ministry of Education (MOE) and National Research Foundation of Korea(NRF) through the Human Resource Training Project for Regional Innovation (NO. NRF-2013H1B8A2032122). |
|
Address: Rm. 104, Changwon Exhibition & Convention Center(CECO), 362, Wonidae-ro, Uichang-gu, Changwon City, Gyeongsangnam-do, Korea
Tel : +82-55-212-1337, Fax : +82-55-212-1331, E-mail : kj-ceramics31@changwon.ac.kr
copyright@GNA International All rights reserved. since 2006